SAE AMS6408 Steel, Hotwork Tool, Bars and Forgings, 5.2Cr - 1.5Mo - 1.0V (0.35-0.45C) (H-13), Electroslag Remelted (ESR)
作者:标准资料网 时间:2024-04-29 03:10:38 浏览:9925
来源:标准资料网
下载地址: 点击此处下载
Product Code:SAE AMS6408
Title:Steel, Hotwork Tool, Bars and Forgings, 5.2Cr - 1.5Mo - 1.0V (0.35-0.45C) (H-13), Electroslag Remelted (ESR) or Consumable Electrode Vacuum Arc Remelted (VAR) Annealed
Issuing Committee:Ams E Carbon And Low Alloy Steels Committee
Scope:This specification covers a premium aircraft quality, low alloy steel in the form of bars, forgings, and forging stock.These products have been used typically for hotwork tooling or for parts requiring a steel capable of through hardening to a minimum hardness of 50 HRC in section thicknesses up to 12 inches (305 mm) with relatively high levels of strength, fatigue resistance, ductility, and thermal stability for use in service from 100 to +1000 °F ( 73 to 538 °C) and where such parts may require welding, but usage is not limited to such applications.Certain design and processing procedures may cause these products to become susceptible to stress-corrosion cracking after heat treatment. ARP1110 recommends practices to minimize such conditions.
Title:Steel, Hotwork Tool, Bars and Forgings, 5.2Cr - 1.5Mo - 1.0V (0.35-0.45C) (H-13), Electroslag Remelted (ESR) or Consumable Electrode Vacuum Arc Remelted (VAR) Annealed
Issuing Committee:Ams E Carbon And Low Alloy Steels Committee
Scope:This specification covers a premium aircraft quality, low alloy steel in the form of bars, forgings, and forging stock.These products have been used typically for hotwork tooling or for parts requiring a steel capable of through hardening to a minimum hardness of 50 HRC in section thicknesses up to 12 inches (305 mm) with relatively high levels of strength, fatigue resistance, ductility, and thermal stability for use in service from 100 to +1000 °F ( 73 to 538 °C) and where such parts may require welding, but usage is not limited to such applications.Certain design and processing procedures may cause these products to become susceptible to stress-corrosion cracking after heat treatment. ARP1110 recommends practices to minimize such conditions.